Preparation of Light-Emitting Ytterbium-Doped Tantalum-Oxide Thin Films Using a Simple Co-Sputtering Method

Read  full  paper  at:
http://www.scirp.org/journal/PaperInformation.aspx?PaperID=54123#.VO2K2yzQrzE

ABSTRACT
Light-emitting ytterbium-doped tantalum-oxide thin films were prepared using a simple co-sputtering method for the first time. Sharp photoluminescence peaks having a wavelength of around 980 nm were observed from films annealed from 700°C to 1000°C for 10 to 40 min. The strongest intensity of the 980-nm peak was obtained from a film deposited using three ytterbium-oxide pellets and annealed at 800°C for 20 min. Such rare-earth doped tantalum-oxide sputtered films can be used as high-refractive-index materials of autocloned photonic crystals that can be applied to novel light-emitting devices, and they will also be used as both anti-reflection and down-conversion layers for realizing high-efficiency silicon solar cells.
 
Cite this paper
Miura, K. , Kano, K. , Arai, Y. and Hanaizumi, O. (2015) Preparation of Light-Emitting Ytterbium-Doped Tantalum-Oxide Thin Films Using a Simple Co-Sputtering Method. Materials Sciences and Applications, 6, 209-213. doi: 10.4236/msa.2015.62024.
 
References
[1]Hanaizumi, O., Miura, K., Saito, M., Sato, T., Kawakami, S., Kuramochi, E. and Oku, S. (2000) Frontiers Related with Automatic Shaping of Photonic Crystals. IEICE Transactions on Electronics, E83-C, 912-919.
 
[2]Sato, T., Miura, K., Ishino, N., Ohtera, Y., Tamamura, T. and Kawakami, S. (2002) Photonic Crystals for the Visible Range Fabricated by Autocloning Technique and Their Application. Optical and Quantum Electronics, 34, 63-70.
http://dx.doi.org/10.1023/A:1013382711983
 
[3]Miura, K., Ohtera, Y., Ohkubo, H., Akutsu, N. and Kawakami, S. (2003) Reduction of Propagation and Bending Losses of Hetero-Structured Photonic Crystal Waveguides by Use of a High-?Structure. Optics Letters, 28, 734-736.
http://dx.doi.org/10.1364/OL.28.000734
 
[4]Cid, M., Stem, N., Brunetti, C., Beloto, A.F. and Ramos, C.A.S. (1998) Improvements in Anti-Reflection Coatings for High-Efficiency Silicon Solar Cells. Surface and Coatings Technology, 106, 117-120.
http://dx.doi.org/10.1016/S0257-8972(98)00499-X
 
[5]Zhu, M., Zhang, Z. and Miao, W. (2006) Intense Photoluminescence from Amorphous Tantalum Oxide Films. Applied Physics Letters, 89, Article ID: 021915. http://dx.doi.org/10.1063/1.2219991
 
[6]Miura, K., Miyazaki, H. and Hanaizumi, O. (2008) Observation of Blue-Light Emission from Tantalum Oxide Films Deposited by Radio-Frequency Magnetron Sputtering. IEICE Transactions on Electronics, E91-C, 1669-1672.
 
[7]Sanada, T., Wakai, Y., Nakashita, H., Matsumoto, T., Yogi, C., Ikeda, S., Wada, N. and Kojima, K. (2010) Preparation of Eu3+-Doped Ta2O5 Phosphor Particles by Sol-Gel Method. Optical Materials, 33, 164-169.
http://dx.doi.org/10.1016/j.optmat.2010.08.018
 
[8]Singh, M.K., Fusegi, G., Kano, K., Bange, J.P., Miura, K. and Hanaizumi, O. (2009) Intense Photoluminescence from Erbium-Doped Tantalum Oxide Thin Films Deposited by Sputtering. IEICE Electronics Express, 6, 1676-1682.
http://dx.doi.org/10.1587/elex.6.1676
 
[9]Singh, M.K., Miura, K., Fusegi, G., Kano, K. and Hanaizumi, O. (2013) Visible-Light Emission Properties of Erbium- Doped Tantalum-Oxide Films Produced by Co-Sputtering. Key Engineering Materials, 534, 154-157.
http://dx.doi.org/10.4028/www.scientific.net/KEM.534.154
 
[10]Miura, K., Arai, Y., Osawa, T. and Hanaizumi, O. (2012) Light-Emission Properties of Europium-Doped Tantalum- Oxide Thin Films Deposited by Radio-Frequency Magnetron Sputtering. Journal of Light and Visual Environment, 36, 64-67. http://dx.doi.org/10.2150/jlve.36.64
 
[11]Miura, K., Osawa, T., Yokota, Y., Suzuki, T. and Hanaizumi, O. (2014) Fabrication of Tm-Doped Ta2O5 Thin Films Using a Co-Sputtering Method. Results in Physics, 4, 148-149.
http://dx.doi.org/10.1016/j.rinp.2014.08.011
 
[12]Miura, K., Osawa, T., Yokota, Y. and Hanaizumi, O. (2014) Fabrication and Evaluation of Ta2O5:Y2O3 Co-Sputtered Thin Films. Results in Physics, 4, 185-186. http://dx.doi.org/10.1016/j.rinp.2014.09.004
 
[13]Ueda, J. and Tanabe, S. (2011) Broadband near Ultra Violet Sensitization of 1 μm Luminescence in Yb3+-Doped CeO2 Crystal. Journal of Applied Physics, 110, Article ID: 073104.
http://dx.doi.org/10.1063/1.3642984
 
[14]Rodriguez, V.D., Tikhomirov, V.K., Mendez-Ramos, J., Yanes, A.C. and Moshchalkov, V.V. (2010) Towards Broad Range and Highly Efficient Down-Conversion of Solar Spectrum by Er3+-Yb3+ Co-Doped Nano-Structured Glass-Ce- ramics. Solar Energy Materials and Solar Cells, 94, 1612-1617. http://dx.doi.org/10.1016/j.solmat.2010.04.081                                                                                                      eww150225lx
标签：

评论

发表评论

此博客中的热门博文

Does Immigration Promote the Investment of the Monopolistic Firm?

In the present paper, we examine the effect of increasing uncertainty of immigrants’ growth on the optimal timing of investment of a firm that has a monopolistic power over the labor market. It is revealed that when the uncertainty of immigrants’ growth is more than a threshold level, increasing uncertainty of immigrants’ growth accelerates the optimal timing of firms’ investment and enhances the economic growth, even if the uncertainty of immigrants’ growth is formulated by the geometric Brownian motion, which is in sharp contrast to the standard result that an increase in the uncertainty postpones the optimal timing. With an increase in the immigrants over the past ten years, workforces in the host countries have been growing significantly to the extent that the immigrants represent 70% of the increase in the workforce in Europe, and 47% in the United States as OECD indicates. In the present paper, we attempted to investigate the effect of increased uncertainty caused by the growi...
发表评论
阅读全文

Education Policy Implementation: A Mechanism for Enhancing Primary Education Development in Zanzibar

Education is one of the fundamental rights of individuals; therefore, the government of a country needs to develop and strengthen educational policy and quality as well as to ensure that everyone has equal access to basic education. The improvement of access and quality of education in the world is becoming as an essential factor in development, whereas the basic education (primary school), is acknowledged as a foundation of the higher educational development for every country. To fulfill this goal, governments introduce several policies and procedures; however, it requires some reforms and participation from the politician, policymakers, and other stakeholders to re-examine educational policy so that it can lead to multiplication and betterment of the reforms. Educational reforms actually focus on accountability. A positive educational development and reform is very challenging and needs more effort and strategy on how to use and utilize the resources effectively as such it can achie...
发表评论
阅读全文