Electrochemical Characterization of Rapid Discharge Sintering (RDS) NiO Cathodes for Dye-Sensitized Solar Cells of p-Type

Read  full  paper  at:
http://www.scirp.org/journal/PaperInformation.aspx?PaperID=53430#.VMWlBSzQrzE

ABSTRACT
Nickel oxide (NiO) thin films with thickness ranging in the interval 0.2 - 3.5 μm have been deposited onto conductive transparent substrate via the method of plasma-assisted rapid discharge sintering (RDS) with microwave heating starting from NiO nanoparticles with diameter 50 nm. The optical and electrochemical properties of the RDS NiO films in the pristine state were characterized in non aqueous electrolyte with the solvent 3-methoxy-propionitrile (3-MPN). Upon electrochemical cycling of NiO in 3-MPN we observed two characteristic oxidation peaks referring to the two nickel centred processes Ni(II)→Ni(III) and Ni(III)→Ni(IV), which are both localized prevalently on the surface of the metallic oxide. The oxide films prepared with the RDS method were also sensitized with different types of commercial dyes, either organometallic (N719, black dye) or organic (squaraine 2, erythrosine B), to compare the corresponding p-type dye-sensitized solar cells (p-DSCs). All dyes here employed matched the energies of their frontier orbitals with the upper edge of NiO valence band and the redox level of the triiodide/iodide couple. The comparison of the performances of the p-DSCs based on RDS NiO which differed exclusively for the nature of the sensitizer showed that the extent of electronic conjugation in the structure of the dye is crucial for the control of the photovoltaic performance of the corresponding p-DSC.
 
Cite this paper
Novelli, V. , Awais, M. , Dowling, D. and Dini, D. (2015) Electrochemical Characterization of Rapid Discharge Sintering (RDS) NiO Cathodes for Dye-Sensitized Solar Cells of p-Type. American Journal of Analytical Chemistry, 6, 176-187. doi: 10.4236/ajac.2015.62016.
 
References
[1]Adler, D. and Feinleib, J. (1970) Electrical and Optical Properties of Narrow-Band Materials. Physical Review B, 2, 3112-3134.
http://dx.doi.org/10.1103/PhysRevB.2.3112
 
[2]Lang, J.W., Kong, L.B., Liu, M., Luo, Y.C. and Kang, L.J. (2010) Asymmetric Supercapacitors Based on Stabilized α-Ni(OH)2 and Activated Carbon. Journal of Solid State Electrochemistry, 14, 1533-1539.
http://dx.doi.org/10.1007/s10008-009-0984-1
 
[3]Decker, F., Passerini, S., Pileggi, R. and Scrosati, B. (1992) The Electrochromic Process in Non-Stoichiometric Nickel Oxide Thin Film Electrodes. Electrochimica Acta, 37, 1033-1038.
http://dx.doi.org/10.1016/0013-4686(92)85220-F
 
[4]Estrada, W., Andersson, A.M., Granqvist, C.G., Gorenstein, A. and Decker, F. (1991) Infrared Reflectance Spectroscopy of Electrochromic NiOxHy Films Made by Reactive dc Sputtering. Journal of Materials Research, 6, 1715-1719.
http://dx.doi.org/10.1557/JMR.1991.1715
 
[5]Tong, L., Iwase, A., Nattestad, A., Bach, U., Weidelener, M., Götz, G., Mishra, A., Bäuerle, P., Amal, R., Wallace, G.G. and Mozer, A.J. (2012) Sustained Solar Hydrogen Generation Using a Dye-Sensitised NiO Photocathode/BiVO4 Tandem Photo-Electrochemical Device. Energy & Environmental Science, 5, 9472-9475.
 
[6]Li, L., Duan, L., Wen, F., Li, C., Wang, M., Hagfeldt, A. and Sun, L. (2012) Visible Light Driven Hydrogen Production from a Photo-Active Cathode Based on a Molecular Catalyst and Organic Dye-Sensitized p-Type Nanostructured NiO. Chemical Communications, 48, 988-990.
http://dx.doi.org/10.1039/c2cc16101j
 
[7]Li, L., Gibson, E.A., Qin, P., Boschloo, G., Gorlov, M., Hagfeldt, A. and Sun, L. (2010) Double-Layered NiO Photocathodes for p-Type DSSCs with Record IPCE. Advanced Materials, 22, 1759-1762.
http://dx.doi.org/10.1002/adma.200903151
 
[8]Nattestad, A., Mozer, A.J., Fischer, M.K.R., Cheng, Y.B., Mishra, A., Bäuerle, P. and Bach, U. (2010) Highly Efficient Photocathodes for Dye-Sensitized Tandem Solar Cells. Nature Materials, 9, 31-35.
 
[9]Irwin, M.D., Buchholz, D.B., Hains, A.W., Chang, R.P.H. and Marks, T.J. (2008) p-Type Semiconducting Nickel Oxide as an Efficiency-Enhancing Anode Interfacial Layer in Polymer Bulk-Heterojunction Solar Cells. Proceedings of the National Academy of Sciences of the United States of America, 105, 2783-2787.
http://dx.doi.org/10.1073/pnas.0711990105
 
[10]Hüfner, S. (1994) Electronic Structure of NiO and Related 3d-Transition-Metal Compounds. Advances in Physics, 43, 183-356.
http://dx.doi.org/10.1080/00018739400101495
 
[11]O’Regan, B. and Grätzel, M. (1991) A Low-Cost, High-Efficiency Solar Cell Based on Dye-Sensitized Colloidal TiO2 Films. Nature, 353, 737-740.
http://dx.doi.org/10.1038/353737a0
 
[12]He, J., Lindsträm, H., Hagfeldt, A. and Lindquist, S.E. (2000) Dye-Sensitized Nanostructured Tandem Cell-First Demonstrated Cell with a Dye-Sensitized Photocathode. Solar Energy Materials and Solar Cells, 62, 265-273.
http://dx.doi.org/10.1016/S0927-0248(99)00168-3
 
[13]Sumikura, S., Mori, S., Shimizu, S., Usami, H. and Suzuki, E. (2008) Syntheses of NiO Nanoporous Films Using Nonionic Triblock Co-Polymer Templates and Their Application to Photo-Cathodes of p-Type Dye-Sensitized Solar Cells. Journal of Photochemistry and Photobiology A, 199, 1-7.
http://dx.doi.org/10.1016/j.jphotochem.2008.04.007
 
[14]Powar, S., Wu, Q., Weidelener, M., Nattestad, A., Hu, Z., Mishra, A., Bäuerle, P., Spiccia, L., Cheng, Y.B. and Bach, U. (2012) Improved Photocurrents for p-Type Dye-Sensitized Solar Cells Using Nano-Structured Nickel(II) Oxide Microballs. Energy & Environmental Science, 5, 8896-8900.
 
[15]Awais, M., Rahman, M., Don MacElroy, J.M., Dini, D., Vos, J.G. and Dowling, D.P. (2011) Application of a Novel Microwave Plasma Treatment for the Sintering of Nickel Oxide Coatings for Use in Dye-Sensitized Solar Cells. Surface and Coatings Technology, 205, S245-S249.
http://dx.doi.org/10.1016/j.surfcoat.2011.01.020
 
[16]Qin, P., Zhu, H., Edvinsson, T., Boschloo, G., Hagfeldt, A. and Sun, L. (2008) Design of an Organic Chromophore for p-Type Dye-Sensitized Solar Cells. Journal of the American Chemical Society, 130, 8570-8571.
http://dx.doi.org/10.1021/ja8001474
 
[17]Odobel, F., Pellegrin, Y., Gibson, E.A., Hagfeldt, A., Smeigh, A.L. and Hammarström, L. (2012) Recent Advances and Future Directions to Optimize the Performances of p-Type Dye-Sensitized Solar Cells. Coordination Chemistry Reviews, 256, 2414-2423.
http://dx.doi.org/10.1016/j.ccr.2012.04.017
 
[18]Minoura, H. and Yoshida, T. (2008) Electrodeposition of ZnO/Dye Hybrid Thin Films for Dye-Sensitized Solar Cells. Electrochemistry, 76, 109-117.
http://dx.doi.org/10.5796/electrochemistry.76.109
 
[19]Murakami, T.N. and Grätzel, M. (2008) Counter Electrodes for DSC: Application of Functional Materials as Catalysts. Inorganica Chimica Acta, 361, 572-580.
http://dx.doi.org/10.1016/j.ica.2007.09.025
 
[20]Gibson, E.A., Awais, M., Dini, D., Dowling, D.P., Pryce, M.T., Vos, J.G., Boschloo, G. and Hagfeldt, A. (2013) Dye Sensitised Solar Cells with Nickel Oxide Photocathodes Prepared via Scalable Microwave Sintering. Physical Chemistry Chemical Physics, 15, 2411-2420.
http://dx.doi.org/10.1039/c2cp43592f
 
[21]Awais, M., Dini, D., Don MacElroy, J.M., Halpin, Y., Vos, J.G. and Dowling, D.P. (2013) Electrochemical Characterization of NiO Electrodes Deposited via a Scalable Powder Microblasting Technique. Journal of Electroanalytical Chemistry, 689, 185-192.
http://dx.doi.org/10.1016/j.jelechem.2012.11.025
 
[22]Halme, J., Saarinen, J. and Lund, P. (2006) Spray Deposition and Compression of TiO2 Nanoparticle Films for Dye-Sensitized Solar Cells on Plastic Substrates. Solar Energy Materials and Solar Cells, 90, 887-899.
http://dx.doi.org/10.1016/j.solmat.2005.05.013
 
[23]Awais, M., Gibson, E., Vos, J.G., Dowling, D.P., Hagfeldt, A. and Dini, D. (2014) Fabrication of Efficient NiO Photocathodes Prepared via RDS with Novel Routes of Substrate Processing for p-Type Dye-Sensitized Solar Cells. Chem-ElectroChem, 1, 384-391.
http://dx.doi.org/10.1002/celc.201300178
 
[24]McConnell, M.L., Dowling, D.P., Pope, C., Donnelly, K., Ryder, A.G. and O’Connor, G.M. (2002) High Pressure Diamond and Diamond-Like Carbon Deposition Using a Microwave CAP Reactor. Diamond and Related Materials, 11, 1036-1040.
http://dx.doi.org/10.1016/S0925-9635(01)00637-9
 
[25]Giustini, M., Angelone, D., Parente, M., Dini, D., Decker, F., Lanuti, A., Reale, A., Brown, T. and Di Carlo, A. (2013) Emission Spectra and Transient Photovoltage in Dye-Sensitized Solar Cells under Stress Tests. Journal of Applied Electrochemistry, 43, 209-215.
http://dx.doi.org/10.1007/s10800-012-0484-3
 
[26]Marrani, A.G., Novelli, V., Sheehan, S., Dowling, D.P. and Dini, D. (2014) Probing the Redox States at the Surface of Electroactive Nanoporous NiO Thin Films. ACS Applied Materials & Interfaces, 6, 143-152.
http://dx.doi.org/10.1021/am403671h
 
[27]Boschloo, G. and Hagfeldt, A. (2001) Spectroelectrochemistry of Nanostructured NiO. Journal of Physical Chemistry B, 105, 3039-3044.
http://dx.doi.org/10.1021/jp003499s
 
[28]Passerini, S., Scarminio, J., Scrosati, B., Zane, D. and Decker, F. (1993) Thin Metal Oxide Films on Transparent Substrates for Li-Insertion Devices. Journal of Applied Electrochemistry, 23, 1187-1195.
http://dx.doi.org/10.1007/BF00625594
 
[29]Passerini, S. and Scrosati, B. (1994) Characterization of Nonstoichiometric Nickel Oxide Thin-Film Electrodes. Journal of the Electrochemical Society, 141, 889-895.
http://dx.doi.org/10.1149/1.2054853
 
[30]Masetti, E., Decker, F. and Dini, D. (1995) The Electrochromic Response of Tungsten Bronzes MxWO3 with Different Ions and Insertion Rates. Solar Energy Materials and Solar Cells, 39, 301-307.
http://dx.doi.org/10.1016/0927-0248(95)00049-6
 
[31]Dini, D. and Decker, F. (1998) Stress in Thin Films of Metal Oxide Electrodes for Intercalation Reactions. Electrochimica Acta, 43, 2919-2923.
http://dx.doi.org/10.1016/S0013-4686(98)00032-2
 
[32]Wherens-Dijksma, M. and Notten, P.H.L. (2006) Electrochemical Quartz Microbalance Characterization of Ni(OH)2-Based Thin Film Electrodes. Electrochimica Acta, 51, 3609-3621.
http://dx.doi.org/10.1016/j.electacta.2005.10.022
 
[33]Beverskog, B. and Puigdomenech, I. (1997) Revised Pourbaix Diagrams for Nickel at 25℃ - 300℃. Corrosion Science, 39, 969-980.
http://dx.doi.org/10.1016/S0010-938X(97)00002-4
 
[34]Awais, M., Dowling, D.D., Rahman, M., Vos, J.G., Decker, F. and Dini, D. (2013) Spray-Deposited NiOx Films on ITO Substrates as Photoactive Electrodes for p-Type Dye-Sensitized Solar Cells. Journal of Applied Electrochemistry, 43, 191-197.
http://dx.doi.org/10.1007/s10800-012-0506-1
 
[35]Hagfeldt, A., Boschloo, G., Sun, L., Kloo, L. and Pettersson, H. (2010) Dye-Sensitized Solar Cells. Chemical Reviews, 110, 6595-6663.
http://dx.doi.org/10.1021/cr900356p
 
[36]Nattestad, A., Ferguson, M., Kerr, R., Cheng, Y.B. and Bach, U. (2008) Dye-Sensitized Nickel(II)oxide Photocathodes for Tandem Solar Cell Applications. Nanotechnology, 19, Article ID: 295304.
http://dx.doi.org/10.1088/0957-4484/19/29/295304
 
[37]Chang, C.H., Chen, Y.C., Hsu, C.Y., Chou, H.H. and Lin, J.T. (2012) Squaraine-Arylamine Sensitizers for Highly Efficient p-Type Dye-Sensitized Solar Cells. Organic Letters, 14, 4726-4729.
http://dx.doi.org/10.1021/ol301860w
 
[38]Venditti, I., Barbero, N., Russo, M.V., Di Carlo, A., Decker, F., Fratoddi, I., Barolo, C. and Dini, D. (2014) Electrodeposited ZnO with Squaraine Sentisizers as Photoactive Anode of DSCs. Materials Research Express, 1, Article ID: 015040.
http://dx.doi.org/10.1088/2053-1591/1/1/015040                                                                eww150126lx
标签：

评论

发表评论

此博客中的热门博文

Does Immigration Promote the Investment of the Monopolistic Firm?

In the present paper, we examine the effect of increasing uncertainty of immigrants’ growth on the optimal timing of investment of a firm that has a monopolistic power over the labor market. It is revealed that when the uncertainty of immigrants’ growth is more than a threshold level, increasing uncertainty of immigrants’ growth accelerates the optimal timing of firms’ investment and enhances the economic growth, even if the uncertainty of immigrants’ growth is formulated by the geometric Brownian motion, which is in sharp contrast to the standard result that an increase in the uncertainty postpones the optimal timing. With an increase in the immigrants over the past ten years, workforces in the host countries have been growing significantly to the extent that the immigrants represent 70% of the increase in the workforce in Europe, and 47% in the United States as OECD indicates. In the present paper, we attempted to investigate the effect of increased uncertainty caused by the growi...
发表评论
阅读全文

Education Policy Implementation: A Mechanism for Enhancing Primary Education Development in Zanzibar

Education is one of the fundamental rights of individuals; therefore, the government of a country needs to develop and strengthen educational policy and quality as well as to ensure that everyone has equal access to basic education. The improvement of access and quality of education in the world is becoming as an essential factor in development, whereas the basic education (primary school), is acknowledged as a foundation of the higher educational development for every country. To fulfill this goal, governments introduce several policies and procedures; however, it requires some reforms and participation from the politician, policymakers, and other stakeholders to re-examine educational policy so that it can lead to multiplication and betterment of the reforms. Educational reforms actually focus on accountability. A positive educational development and reform is very challenging and needs more effort and strategy on how to use and utilize the resources effectively as such it can achie...
发表评论
阅读全文